PRODUCTS
Polyester Powder Resin Saturated carboxylated polyester powder resins / TGIC system
| Urefree |
Ratio |
Curing t(min.)/T(oC) |
Acid value (mg.KOH/g.) |
Melt viscosity at 165oC (Poises) |
Glass transition (oC) |
Feature |
PDF |
| 4001 |
90-10 |
10'/ 200oC |
50-55 |
100-300 |
62 |
For matt paints by dry blend with UREFREE®4501,Gas oven stability and outdoor resistance. |
|
| 4401 |
96-4 |
10'/ 200oC |
20-25 |
400-600 |
57 |
For matt paint by dry blend with UREFREE®4001 and gas oven stability. |
|
| 4501 |
95-5 |
10'/ 200oC |
22-26 |
400-600 |
62 |
For matt paint by dry blend with UREFREE® 4001 and gas oven stability. High Tg than UREFREE® 4401. |
|
| 4704 |
93-7 |
10'/ 200oC |
30-36 |
250-450 |
66 |
Excellent flow and outdoor durability. |
|
| 4704IM |
93-7 |
10'/ 200oC |
30-36 |
300-500 |
62 |
Excellent flow, good balance properties and good outdoor durability. |
|
| 4706 |
93-7 |
10'/ 200oC |
30-36 |
300-500 |
64 |
TGIC with excellent weathering resistance. |
|
| 4707 |
93-7 |
10'/ 200oC |
30-36 |
400-600 |
65 |
Good flow, Slow cure and high Tg. |
|
| 4708 |
93-7 |
10'/ 200oC |
30-36 |
400-600 |
67 |
Very good flow, good mechanical properties, high gloss and high Tg. |
|
| 4761 |
93-7 |
10'/ 160oC |
30-36 |
200-400 |
60 |
Good balance between high reactivity, goodmechanical properties and good outdoor durability. |
|
| 4762 |
93-7 |
t10'/ 160oC |
30-36 |
200-400 |
60 |
Good balance between high reactivity, good mechanical properties and good chemical resistance. |
|
| 4763 |
93-7 |
10'/ 160oC |
30-36 |
200-400 |
60 |
Excellent flow, high reactivity and good mechanical properties. |
|
| 4780 |
93-7 |
10'/ 180oC |
30-36 |
500-700 |
68 |
High Tg, good flow and outdoor durability. |
|
| 4784 |
93-7 |
10'/ 180oC |
30-36 |
300-500 |
62 |
Good flow, medium cure and good outdoor durability. |
|
| 4789 |
93-7 |
10'/ 180oC |
30-36 |
400-600 |
64 |
Good flow, medium cure, high Tg and good outdoor durability. |
|
Saturated carboxylated polyester powder resins / HYBRID system; ratio: 80/20
| Urefree |
Ratio |
Curing t(min.)/T(oC) |
Acid value (mg.KOH/g.) |
Melt viscosity at 165oC (Poises) |
Glass transition (oC) |
Feature |
PDF |
| 6280 |
80-20 |
10'/ 180oC |
18-22 |
400-600 |
58 |
Good mechanical properties. Excellent matting character. |
|
Saturated carboxylated polyester powder resins / HYBRID system; ratio: 70/30
| Urefree |
Ratio |
Curing t(min.)/T(oC) |
Acid value (mg.KOH/g.) |
Melt viscosity at 165oC (Poises) |
Glass transition (oC) |
Feature |
PDF |
| 6462 |
70-30 |
10'/ 160oC |
30-36 |
300-500 |
56 |
High reactivity. |
|
| 6463new |
70-30 |
10'/ 160oC |
30-36 |
300-500 |
60 |
New generation hybrid high Tg version 6462. |
|
| 6482 |
70-30 |
10'/ 180oC |
30-36 |
300-500 |
56 |
Good mechanical properties, very good chemical resistance and good for clear. |
|
| 6485 |
70-30 |
10'/ 180oC |
30-36 |
400-550 |
61 |
Excellent flow, good over baking resistance and high Tg for better storage stability. |
|
| 6489 |
70-30 |
15'/ 180oC |
30-36 |
300-500 |
59 |
Good flow, mechanical and yellowing resistance. |
|
| 6489IM |
70-30 |
10'/ 180oC |
30-36 |
300-450 |
60 |
Excellent flow, good mechanical properties and good over baking resistance. |
|
| 6489-T |
70-30 |
10'/ 180oC |
30-36 |
300-450 |
60 |
Tribo version 6489 |
|
| 6780 |
70-30 |
10'/ 180oC |
30-36 |
200-400 |
56 |
New generation hybrid, good balance of properties, good over baking with gas fire and can be used for making the structure finish. |
|
| 6783new |
70-30 |
10'/ 180oC |
30-35 |
500-700 |
62 |
Good flow and high gloss. Good mechanical properties and flexibility. High Tg excellent storage stability. |
|
| 7030S |
70-30 |
10'/ 180oC |
30-36 |
250-450 |
56 |
Good balance of properties and can be used for matte and structure finish. |
|
| 7030SIM |
70-30 |
10'/ 180oC |
30-36 |
200-400 |
56 |
Good flow and good balance of properties, high gloss. |
|
Saturated carboxylated polyester powder resins / HYBRID system; ratio: 60/40
| Urefree |
Ratio |
Curing t(min.)/T(oC) |
Acid value (mg.KOH/g.) |
Melt viscosity at 165oC (Poises) |
Glass transition (oC) |
Feature |
PDF |
| 6668new |
60-40 |
10'/ 160oC |
45-55 |
200-400 |
61 |
High reactivity, New generation Hybrid, high Tg for better storage stability, high flexibility and good flow. |
|
| 6669IM |
60-40 |
10'/160°C |
45-55 |
100-300 |
60 |
High reactivity excellent flow good balance properties. |
|
| 6681E |
60-40 |
10'/ 180oC |
40-50 |
300-500 |
60 |
General purpose, good flow and good mechanical properties. High Tg and can be used for structure finish. |
|
| 6686 |
60-40 |
10'/ 180oC |
50-56 |
100-250 |
55 |
Excellent flow, good balance properties can be used for matte finish. |
|
| 6687new |
60-40 |
10'/ 180oC |
45-55 |
100-150 at 200 oC |
73 |
High Tg, good stability, high mechanical properties. |
|
| 6689new |
60-40 |
10'/ 180oC |
40-50 |
300-500 |
62 |
Economic grade, Excellent flow, Good mechanical prop. High Tg good storage stability |
|
Saturated carboxylated polyester powder resins / HYBRID system; ratio: 50/50
| Urefree |
Ratio |
Curing t(min.)/T(oC) |
Acid value (mg.KOH/g.) |
Melt viscosity at 165oC (Poises) |
Glass transition (oC) |
Feature |
PDF |
| 6883 |
50-50 |
10'/ 180oC |
70-80 |
100-300 |
66 |
Excellent flow, gloss, high Tg for better storage stability and yellowing resistance. |
|
| 6884 |
50-50 |
10'/ 180oC |
70-80 |
100-300 |
60 |
Excellent combination of cure, good flow and high chemical resistance. |
|
| 6884-T |
50-50 |
10'/ 180oC |
70-80 |
100-300 |
60 |
Tribo version 6884 |
|
| 6885 |
50-50 |
10'/ 180oC |
70-80 |
100-300 |
57 |
Excellent combination of cure, Excellent flow. General purpose. |
|
| 6887new |
50-50 |
10'/ 180oC |
70-80 |
100-300 |
66 |
General purpose with good flow and high Tg for better storage stability. |
|
Saturated carboxylated polyester powder resins / HYBRID system; ratio: 55/45
| Urefree |
Ratio |
Curing t(min.)/T(oC) |
Acid value (mg.KOH/g.) |
Melt viscosity at 165oC (Poises) |
Glass transition (oC) |
Feature |
PDF |
| 6870 |
55-45 |
10'/ 170oC |
70-80 |
100-300 |
60 |
High reactivity and excellent flow. |
|
Saturated carboxylated polyester powder resins / b-hydroxyalkylamide curing agents (Primid)
| Urefree |
Ratio |
Curing t(min.)/T(oC) |
Acid value (mg.KOH/g.) |
Melt viscosity at 165oC (Poises) |
Glass transition (oC) |
Feature |
PDF |
| 8180 |
90-10 |
10' / 180oC |
70-76 |
100-300 |
61 |
To be combine with 8180 alone or with 8300 for matt powder coatings by dry blending. Different glosses depending on 8300/8180 mixing ratios. |
|
| 8300 |
96.5-3.5 |
10' / 200oC |
22-28 |
300-500 |
56 |
Low Primid demand of matt dry blend system in combination with high demand Primid resin. Optimized weathering resistance. |
|
| 8305new |
96.5-3.5 |
10' / 200oC |
22-26 |
40-65
(REL 200C°) |
58 |
Excellent leveling and good outdoor durability. Good flow high gloss, good yellowing resistance |
|
| 8500 |
95-5 |
10' / 200oC |
30-36 |
200-400 |
62 |
Super-durable resin, Good flow with high functionality. |
|
| 8580 |
95-5 |
10' / 180oC |
30-36 |
200-400 |
58 |
General propose. Good flow, optimized weathering resistance. |
|
| 8580 -T |
95-5 |
10' / 180oC |
30-36 |
200-400 |
60 |
Tribo version of 8580. |
|
| 8585 |
95-5 |
10' / 180oC |
30-36 |
200-400 |
60 |
General purpose with good flow and low bake Primid. |
|
Saturated hydroxylated polyester powder resins (Polyurethane system)
| Urefree |
Ratio |
Curing t(min.)/T(oC) |
Acid value (mg.KOH/g.) |
Melt viscosity at 165oC (Poises) |
Glass transition (oC) |
Hydroxyl value (mg.KOH/g) |
Feature |
PDF |
| 3000 |
57-43 |
10-20'/ 200oC |
max. 5 |
30-60 at 200 oC |
56 |
150-200 |
High hardness, chemical and stain resistance. Useful for low gloss formulation. |
|
| 3130-J |
90-10 |
10-20’/ 200oC |
max. 10 |
400-600 |
60 |
20-30 |
Low demand isocyanate standard architectural and excellent flow. |
|
| 3300 |
80-20 |
10-20’/ 200oC |
Max. 10 |
200-400 |
56 |
35-45 |
Standard polyurethane resin in industry purpose. |
|
| 3301New |
70-30 |
10-20’/ 200oC |
Max. 10 |
300-500 |
63 |
75-95 |
Very good flow and anti-graffiti |
|
| 9240 |
98-2 |
20'/ 180oC |
max. 10 |
600-900 |
70 |
7-17 |
Good outdoor durability. Crosslinkable with powderlink 1174. |
|
| 9360 |
94-6 |
20'/ 180oC |
max. 8 |
300-800 |
58 |
30-40 |
Special polyester for low gloss structured finishes. Crosslinkable with powderlink 1174. |
|
UREZ. Saturated carboxylated polyester powder resins
| UREZ |
Ratio |
Curing t(min.)/T(oC) |
Acid value (mg.KOH/g.) |
Melt viscosity at 165oC (Poises) |
Glass transition (oC) |
Feature |
PDF |
| T937 |
TGIC 93-7 |
10’/ 200oC |
30-36 |
400-600 |
67 |
Very good flow, good mechanical properties, high gloss and high Tg. |
|
| H558 |
HYBRID 50-50 |
10'/ 180oC |
70-80 |
100-300 |
60 |
Good flow, Good mechanical properties. |
|
| H640 |
HYBRID 60-40 |
10'/ 180oC |
40-50 |
30-50 at 200oC |
56 |
Good flow, Good mechanical properties. |
|
| H738 |
HYBRID 70-30 |
10'/ 180oC |
30-36 |
250-450 |
55 |
Good flow, Good mechanical properties. |
|
Masterbatches with flow promoters
| Urefree |
Ratio |
Curing t(min.)/T(oC) |
Acid value (mg.KOH/g.) |
Melt viscosity at 165oC (Poises) |
Glass transition (oC) |
Feature |
PDF |
| 4700A5 |
- |
- |
25-40 |
100-400 |
60 |
Masterbatch at 5% of acrylic polymer in a carboxylated polyester. |
|
| 4700A10 |
- |
- |
28-36 |
100-300 |
60 |
Masterbatch at 10% of acrylic polymer in a carboxylated polyester. |
|